Fabrication and optical property of colloidal crystal without cracks by using flexible fiber array
| Project/Area Number |
19510106
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Nanostructural science
|
|---|
| Research Institution | Tokyo University of Science |
|---|
Principal Investigator |
KAWAI Takeshi Tokyo University of Science, 工学部, 教授 (10224718)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
近藤 剛史 東京理科大学, 工学部, 助教 (00385535)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000)
Fiscal Year 2008: ¥1,690,000 (Direct Cost: ¥1,300,000、Indirect Cost: ¥390,000)
Fiscal Year 2007: ¥2,860,000 (Direct Cost: ¥2,200,000、Indirect Cost: ¥660,000)
|
|---|
| Keywords | クラスター / 微粒子 / ポリスチレン粒子 / ガラスファイバー / コロイド結晶 / 構造色 / 基板引き上げ法 |
|---|
| Research Abstract |
基板引上げ法によるコロイド結晶作製法は低エネルギーかつ低コストという利点があるが、数十μm間隔でクラックが発生する問題がある。本研究は、基板に柔軟なガラスファイバーを用いてクラックの発生を抑制することを目的とした。様々な条件で評価した結果、ファイバー間にサポートファイバーを配置することにより大面積の無欠陥コロイド結晶が得られることに加え、結晶形成の位置を制御できることが明らかとなった。さらに、無欠陥領域の拡大にはアガロースなどの高分子を加えることが有効であることを見出した。
|