Control of fractal dimension of Si nanocryatal assembly and its effect on the optical properties
| Project/Area Number |
19510112
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Nanostructural science
|
|---|
| Research Institution | Konan University |
|---|
Principal Investigator |
UMEZU Ikurou Konan University, 理工学部, 教授 (30203582)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
杉村 陽 甲南大学, 理工学部, 教授 (30278791)
稲田 貢 関西大学, 工学部, 講師 (00330407)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,160,000 (Direct Cost: ¥3,200,000、Indirect Cost: ¥960,000)
Fiscal Year 2008: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
Fiscal Year 2007: ¥2,860,000 (Direct Cost: ¥2,200,000、Indirect Cost: ¥660,000)
|
|---|
| Keywords | レーザーアブレーション / ナノ結晶 / シリコン / 凝集構造 / フラクタル / 自己組織化 / コアシェル / 光吸収 / コアシェル構造 |
|---|
| Research Abstract |
バックグラウンドガス中でパルスレーザをターゲットに照射するとナノ結晶が生成する。本研究ではバックグラウンドガスにヘリウムと水素の混合ガスを用いナノ結晶を作成することによって、水素による表面水素化とナノ結晶の衝突位置が空間上と基板上で生成したナノ結晶集合体の構造を制御することに成功した。ナノ結晶の集合構造はナノ結晶間の相互作用によってナノ結晶集合体の光学的および電気伝導特性に影響を与えることを明らかにした。
|
Report
(3 results)
Research Products
(56 results)