Studies on the Preparation of the Thin Film of Scallop Shell Ceramics by Dry-Method and the Effects on Improvement of the Quality of Water
| Project/Area Number |
19550155
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Environmental chemistry
|
|---|
| Research Institution | Asahikawa National College of Technology |
|---|
Principal Investigator |
FURUSAKI Atsushi Asahikawa National College of Technology, 物質化学工学科, 教授 (40280317)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,940,000 (Direct Cost: ¥3,800,000、Indirect Cost: ¥1,140,000)
Fiscal Year 2008: ¥520,000 (Direct Cost: ¥400,000、Indirect Cost: ¥120,000)
Fiscal Year 2007: ¥4,420,000 (Direct Cost: ¥3,400,000、Indirect Cost: ¥1,020,000)
|
|---|
| Keywords | 高周波スパッタリング / 酸化カルシウム薄膜 / ホタテ貝殻 / 水質浄化 / ホタテ貝殻焼成物 / 水質浄化材 / 廃棄物再資源化 / 環境材料 |
|---|
| Research Abstract |
「高周波スパッタリング法」によりCaO 薄膜を形成し、成膜条件がその構造や形態、膜厚に及ぼす影響を検討した。その結果、スパッタ時間とともに薄膜はCa(OH)2 単一相からCaO との混合相に変化すること、高周波電源出力はほとんど影響を及ぼさないこと、基板温度が高いとCa(OH)2 のピークが消失し非晶質膜となること、などがわかった。
また、1000℃で焼成した貝殻小片を模擬汚染水(60ppm-COD)中に浸漬すると、COD 値は最大50%程度まで減少することが確かめられた。
|