Synthesis of Alloy Anodes Using Gas-Deposition for Secondary Batteries
| Project/Area Number |
19550179
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Functional materials/Devices
|
|---|
| Research Institution | Tottori University |
|---|
Principal Investigator |
SAKAGUCHI Hiroki Tottori University, 大学院・工学研究科, 教授 (00202086)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
IIDA Takahisa 鳥取大学, 大学院・工学研究科, 助教 (10367138)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000)
Fiscal Year 2008: ¥2,080,000 (Direct Cost: ¥1,600,000、Indirect Cost: ¥480,000)
Fiscal Year 2007: ¥2,600,000 (Direct Cost: ¥2,000,000、Indirect Cost: ¥600,000)
|
|---|
| Keywords | リチウム二次電池 / 負極 / 合金 / ガスデポジション / 二次電池 / リチウム電池 / 負極材料 |
|---|
| Research Abstract |
ケイ素は実用化されている黒鉛よりも大きな充放電容量を持つ反面サイクル寿命に乏しい. 一方, LaGe_2は容量は小さいものの非常に優れたサイクル安定性を示す. ガスデポジション法により作製したLaGe_2/Siコンポジット厚膜電極の放電容量のサイクル依存性をケイ素およびLaGe_2の単独電極の結果と比較したところ, ケイ素由来の高容量にLaGe_2 の優れたサイクル安定性が付与された非常に優れた電極であることがわかった.
|