Improvement of Mechanical Strength for Supramolecular Film due to Molecular Zipper Formation
| Project/Area Number |
19550200
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Polymer/Textile materials
|
|---|
| Research Institution | Chiba University |
|---|
Principal Investigator |
YAMADA Norihiro Chiba University, 教育学部, 教授 (40182547)
|
|---|
| Research Collaborator |
YOSHIDA Sayaka 千葉大学, 教育学研究科, 修士2年
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,810,000 (Direct Cost: ¥3,700,000、Indirect Cost: ¥1,110,000)
Fiscal Year 2008: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000)
Fiscal Year 2007: ¥3,770,000 (Direct Cost: ¥2,900,000、Indirect Cost: ¥870,000)
|
|---|
| Keywords | 自己組織化 / 超薄膜 / 超分子化学 / ナノ材料表面 / 界面物性 / 塑性加工 / ナノ材料 / 表面・界面物 |
|---|
| Research Abstract |
アルキル長鎖を有するヘキサロイシン誘導体は、油圧プレス機を用いて加圧すると、水素結合してできたβ-シート集積体がアミノ酸側鎖間で噛み合う結果、柔軟性と機械強度にすぐれたフィルムになることを、引っ張り強度の測定結果、ならびにFT-IR スペクトルの解析結果から明らかにした。
|