Control of Higher Order Structure by Crystallization via Mesomorphic Phase
| Project/Area Number |
19550204
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Polymer/Textile materials
|
|---|
| Research Institution | Kyoto University |
|---|
Principal Investigator |
NISHIDA Koji Kyoto University, 化学研究所, 准教授 (80189290)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
KANAYA Toshiji 京都大学, 化学研究所, 教授 (20152788)
MATSUBA Go 京都大学, 化学研究所, 助教 (10378854)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000)
Fiscal Year 2008: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
Fiscal Year 2007: ¥3,380,000 (Direct Cost: ¥2,600,000、Indirect Cost: ¥780,000)
|
|---|
| Keywords | 高分子 / メゾ相 / アイソタクチックポリプロピレン / 繊維材料 |
|---|
| Research Abstract |
高輝度のX線源と高速の時分割測定が可能な放射光施設(SPring-8)、および、自ら開発した急冷過程をX線回折装置内で再現する高速温度ジャンプ装置を用いて、アイソタクチックポリプロピレン(iPP)がメゾ相を形成する瞬間のその場観測に成功した。また、iPP以外のメゾ相を形成する結晶性高分子の探索を行い、ポリブチレンナフタレート(PBN)がiPPと類似のメゾ相を形成することを突き止めた。さらに、上述の2種類のメゾ相形成高分子に対して、メゾ相からの加熱過程での結晶化を伴う高次構造形成過程についても示差走査熱量測定、変更解消光透過測定、小角X線散乱等を用いて明らかにした。
|