Fracture phenomena associating with strain-induced density fluctuations in glassy polymers
| Project/Area Number |
19550206
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Polymer/Textile materials
|
|---|
| Research Institution | Kyoto University |
|---|
Principal Investigator |
TAKENAKA Mikihito Kyoto University, 大学院・工学研究科, 講師 (30222102)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
HASEGAWA Hirokazu 京都大学, 大学院・工学研究科, 教授 (60127123)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000)
Fiscal Year 2008: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
Fiscal Year 2007: ¥3,380,000 (Direct Cost: ¥2,600,000、Indirect Cost: ¥780,000)
|
|---|
| Keywords | 高分子材料物性 / 粘弾性効果 / ガラス状高分子 / 延伸誘起密度揺らぎ / ポリメタクリル酸メチル / 小角X線散乱 / ストレスオーバーシュート / 延伸誘起相分離 / クレージング / ソフトマター |
|---|
| Research Abstract |
ガラス状高分子のガラス転移点以下では、密度揺らぎは大きな応力の空間不均一性を生じさせる。その密度に伴う応力の空間不均一性が、延伸下においては粘弾性効果によって密度揺らぎの誘起が起こり、それが非線形粘弾性現象の発現および破壊現象が起こることが明らかになった。
|