Elucidation of the growth mechanism and mechanical properties of semiconductor nanowires via atomistic simulation
| Project/Area Number |
19560077
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Materials/Mechanics of materials
|
|---|
| Research Institution | The University of Electro-Communications |
|---|
Principal Investigator |
SHINTANI Kazuhito The University of Electro-Communications, 電気通信学部, 教授 (00162793)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000)
Fiscal Year 2008: ¥1,690,000 (Direct Cost: ¥1,300,000、Indirect Cost: ¥390,000)
Fiscal Year 2007: ¥2,990,000 (Direct Cost: ¥2,300,000、Indirect Cost: ¥690,000)
|
|---|
| Keywords | ナノ材料 / ナノワイヤ / VLS成長 / クラスター / コアシェル / 積層 / ヤング率 / 分子動力学法 / 一次元ナノ構造 / 積層型 |
|---|
| Research Abstract |
VLS成長機構において触媒として重要な役割を果たすクラスターの特性解析を行い、2個のクラスターの合体過程を調べて、合体後の形態を決定する支配因子は温度とクラスターの大きさであることを明らかにした。また、コアシェル型と軸方向積層型のナノワイヤの引張特性を調べ、コアシェル型ナノワイヤのヤング率は限られたGe分率の範囲で、Vegard則に従うこと、軸方向積層型ナノワイヤのヤング率の方向依存性はほとんどないことが分かった。
|