Study on the Yield Mode Transition in Amorphous Polymeric Materials
| Project/Area Number |
19560081
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Materials/Mechanics of materials
|
|---|
| Research Institution | Kanazawa University |
|---|
Principal Investigator |
KITAGAWA Masayoshi Kanazawa University, 名誉教授 (80007773)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
YAMADA Yoshinori 金沢大学, 機械工学系, 教授 (20126626)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,810,000 (Direct Cost: ¥3,700,000、Indirect Cost: ¥1,110,000)
Fiscal Year 2008: ¥520,000 (Direct Cost: ¥400,000、Indirect Cost: ¥120,000)
Fiscal Year 2007: ¥4,290,000 (Direct Cost: ¥3,300,000、Indirect Cost: ¥990,000)
|
|---|
| Keywords | 非結晶性高分子 / 降伏モード / すべり線成長速度 / 速度過程論 / すべり線密度転位論アナロジー / すべり線密度 / 転位アナロジー / 非結晶性高分子材 / すべり線 / せん断帯 / PET |
|---|
| Research Abstract |
非結晶性の高分子材料について引張およびせん断の変形を行った場合の降伏現象について調べた。低温・高ひずみ速度の場合には、せん断帯が生じて降伏する(LSBモード)。一方、高温・低ひずみ速度の場合には、微細な無数のすべり線の発生と成長のみで降伏する(DSLモード)。また高速・低温でのLSBモードが低速・高温ではDSLモードに遷移することを発見し、降伏モード遷移を規定するひずみ速度・温度条件の実験式を得た。微細なすべり線の成長速度の温度および応力依存依存性はEyringの速度過程論によって説明できる。
|