Evaluation Techniques on Wall Thinning Rate due to Cavitation and Development of Cavitation-Resistant Materials
| Project/Area Number |
19560083
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Materials/Mechanics of materials
|
|---|
| Research Institution | University of Fukui |
|---|
Principal Investigator |
HATTORI Shuji University of Fukui, 大学院・工学研究科, 教授 (00143933)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
MAEKAWA Norihide 福井大学, 工学研究科, 助手 (20262610)
|
|---|
| Project Period (FY) |
2007 – 2009
|
| Project Status |
Completed (Fiscal Year 2009)
|
| Budget Amount *help |
¥4,810,000 (Direct Cost: ¥3,700,000、Indirect Cost: ¥1,110,000)
Fiscal Year 2009: ¥650,000 (Direct Cost: ¥500,000、Indirect Cost: ¥150,000)
Fiscal Year 2008: ¥650,000 (Direct Cost: ¥500,000、Indirect Cost: ¥150,000)
Fiscal Year 2007: ¥3,510,000 (Direct Cost: ¥2,700,000、Indirect Cost: ¥810,000)
|
|---|
| Keywords | 環境強度 / キャビテーション・エロージョン / キャビテーション / Ti-Ni形状記憶合金 / 硬さ |
|---|
| Research Abstract |
本研究では,各種配管材料に用いる鉄鋼材料について長時間の損傷試験を行った.今まで本研究室で得られているデータベースと比較した結果,鉄鋼材料の長時間使用後の損傷量の予測モデルを作成し,損傷量の定式化を行い鉄鋼材料の長時間に対する損傷を評価した.また,配管に施す表面被覆材料にTi-Ni合金の使用を検討し,実際に表面被覆材料を作製し損傷試験を行い,Ti-Ni形状記憶合金が表面被覆材料に適していることを明らかにした.
|