EVALUATION OF MECHANICAL CHARACTERISTICS OF CONICAL PROTRUSIONS FORMED ON SURFACE OF STEELS BY SPUTTER-ETCHING
| Project/Area Number |
19560103
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Materials/Mechanics of materials
|
|---|
| Research Institution | Hiroshima Kokusai Gakuin University |
|---|
Principal Investigator |
NAKASA Keijiro Hiroshima Kokusai Gakuin University, 工学部, 教授 (80034370)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
KATO Masahiko 広島大学, 大学院工学研究科, 准教授 (70274115)
WANG Rongguang 広島工業大学, 工学部, 准教授 (30363021)
|
|---|
| Co-Investigator(Renkei-kenkyūsha) |
KATO Masahiko 広島大学, 大学院工学研究科, 准教授 (70274115)
WANG Rongguang 広島工業大学, 工学部, 准教授 (30363021)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,420,000 (Direct Cost: ¥3,400,000、Indirect Cost: ¥1,020,000)
Fiscal Year 2008: ¥910,000 (Direct Cost: ¥700,000、Indirect Cost: ¥210,000)
Fiscal Year 2007: ¥3,510,000 (Direct Cost: ¥2,700,000、Indirect Cost: ¥810,000)
|
|---|
| Keywords | 構造・機能材料 / プラズマ加工 / ナノ材料 / 円錐形突起物 / 機械的性質 |
|---|
| Research Abstract |
鋼のスパッタエッチングにより形成される微細な円錐状突起物は、多くの電子・機械・化学的機能性をもっている。本研究では、それらの用途開発に重要となる突起物の機械的性質を明らかにするため、腐食試験、引張り試験、スクラッチ試験、圧縮試験などを行なった。その結果、突起物を有する表面は十分な耐食性をもっていること、突起物は素地と強固に密着していて脱落しにくく、じん性・強度に優れていることを明らかにした。
|