Research of the low friction and low wear phenomenon between nano cluster diamond and metal
| Project/Area Number |
19560132
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Design engineering/Machine functional elements/Tribology
|
|---|
| Research Institution | Tohoku University |
|---|
Principal Investigator |
MIKI Hiroyuki Tohoku University, 流体科学研究所, 助教 (80325943)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
TAKAGI Toshiyuki 東北大学, 流体科学研究所, 教授 (20197065)
|
|---|
| Research Collaborator |
TAKENO Takanori 東北大学, 国際高等研究教育機構, 助教 (00451617)
YONEMURA Shigeru 東北大学, 流体科学研究所, 准教授 (00282004)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,290,000 (Direct Cost: ¥3,300,000、Indirect Cost: ¥990,000)
Fiscal Year 2008: ¥1,950,000 (Direct Cost: ¥1,500,000、Indirect Cost: ¥450,000)
Fiscal Year 2007: ¥2,340,000 (Direct Cost: ¥1,800,000、Indirect Cost: ¥540,000)
|
|---|
| Keywords | トライボロジー / ダイヤモンド / 直接シミュレーション・モンテカルロ法 |
|---|
| Research Abstract |
研磨しやすい気相合成ダイヤモンド薄膜を成膜し, この膜を適度に研磨することにより得られる金属との間の低摩擦・低摩耗摺動について定量的に評価した。ダイヤモンド膜は研磨により、相手材金属と接触する平坦部と接触に寄与しない非周期的な溝構造が形成され、潤滑油がなくても相手材金属を摩耗しない摺動を実現することが明らかになった。また、研磨により得られた構造では摩擦係数がほとんど零になる摺動条件があることを計算機シミュレーションにより導き出した。
|