| Project/Area Number |
19560196
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Thermal engineering
|
|---|
| Research Institution | The University of Electro-Communications |
|---|
Principal Investigator |
KUROSAKI Yasuo The University of Electro-Communications, 共同研究センター, 客員教授 (70016442)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
佐藤 公俊 電気通信大学, 共同研究センター, 研究員 (80313419)
|
|---|
| Co-Investigator(Renkei-kenkyūsha) |
SATO Kimitoshi 株式会社キャンパスクリエイト(電気通信大学TLO), 技術開発部, ゼネラルマネージャ (80313419)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,420,000 (Direct Cost: ¥3,400,000、Indirect Cost: ¥1,020,000)
Fiscal Year 2008: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
Fiscal Year 2007: ¥3,120,000 (Direct Cost: ¥2,400,000、Indirect Cost: ¥720,000)
|
|---|
| Keywords | ふく射 / 熱伝導 / ヒートシンク / フッ素樹脂 / COレーザー / オレフィン樹脂 / CO2レーザー |
|---|
| Research Abstract |
レーザー透過放熱体利用の樹脂溶着技術において、COレーザーにより0.5mm厚のPFAフィルムが、溶融一体化されることを確認した。部材最表面から溶融深さを確認した結果0.75mm であったのでこの肉厚までの重ね合せ溶着は可能である。さらに、PFA とPTFE との溶着、および、その他のエンプラ素材(PC,PET,POM,PBT)についてもCO レーザーの適用性を検討し、それぞれ溶着が可能であることを確認した。
|