Study on Improving Luminance Efficiency and Reducing Discharge Voltage in Liquid Crystal Display Back-Lighting Lamp
| Project/Area Number |
19560303
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
電力工学・電気機器工学
|
|---|
| Research Institution | Kanagawa Institute of Technology |
|---|
Principal Investigator |
ARAI Toshihiko Kanagawa Institute of Technology, 工学部, 教授 (60130796)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
GOTO Miki 神奈川工科大学, 工学部, 講師 (70195949)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000)
Fiscal Year 2008: ¥780,000 (Direct Cost: ¥600,000、Indirect Cost: ¥180,000)
Fiscal Year 2007: ¥3,900,000 (Direct Cost: ¥3,000,000、Indirect Cost: ¥900,000)
|
|---|
| Keywords | 光源技術 / ディスプレイ / 液晶バックライト / ネオンプラズマ / 冷陰極 / MgO薄膜 / 放電開始電圧 / 二次電子放出係数 / ダイヤモンド電極 / Mg0薄膜 |
|---|
| Research Abstract |
2007年度および2008年度を通して液晶バックライトに用いる冷陰極蛍光ランプの電極応用としてダイヤモンド基板上にMgOを成膜した複合電極の可能性を検討した。研究成果の概要を以下に列記する。
(1) ダイヤモンド電極上に成膜するMgO薄膜の堆積条件(スパッタリングガスの混合比、基板温度、MgO膜厚)を変えて、製作したMgO薄膜の二次電子放出係数を明らかにし、成膜の最適条件を確立した。
(2) 複合電極の下地として用いるダイヤモンド電極の放電特性への電極表面粗さの影響を検討した結果、表面を粗くすることにより二次電子放出係数が大きくなることを見出した。
(3) Ne/Xe混合ガスプラズマからのXe 原子の共鳴線147nmの真空紫外発光強度はXeガスを30%添加で最大となることがわかった。
|