Fabrication and characterization of multifilamentary Bi-2223 tapes with inter-filament Ni barrier for the practical application to HTS cable.
| Project/Area Number |
19560305
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
電力工学・電気機器工学
|
|---|
| Research Institution | Miyakonojo National College of Technology |
|---|
Principal Investigator |
NOJI Hideki Miyakonojo National College of Technology, 電気情報工学科, 准教授 (30280340)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,420,000 (Direct Cost: ¥3,400,000、Indirect Cost: ¥1,020,000)
Fiscal Year 2008: ¥1,950,000 (Direct Cost: ¥1,500,000、Indirect Cost: ¥450,000)
Fiscal Year 2007: ¥2,470,000 (Direct Cost: ¥1,900,000、Indirect Cost: ¥570,000)
|
|---|
| Keywords | 超電導線材 / Bi-2223 超電導体 / 超電導ケーブル / 高温超電導体 / 超電導テープ / 金属バリア / 臨界電流値 / 臨界電流密度 |
|---|
| Research Abstract |
7 芯Ni バリア超電導テープを作製したが、既存の機器ではNi バリアを十分薄くすることができず、臨界電流値はゼロであった。一方、作製方法の改善で7 芯バリア無し超電導テープの臨界電流値は6.4 A まで向上した。超電導テープの通電損失を評価するため、LabVIEW により自動計測システムを構築した。住友電工および古河電工が作製した超電導ケーブルを対象として交流損失を計算し、測定値と一致する結果を得た。
|