EFFECT OF SMOOTH CRACKS OF ULTRA-HIGH-STRENGTH CONCRETE UPON HYSTERESIS CHARACTERISTICS OF RC COLUMNS
| Project/Area Number |
19560564
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Building structures/materials
|
|---|
| Research Institution | Tokyo Institute of Technology |
|---|
Principal Investigator |
SHINOHARA Yasuji Tokyo Institute of Technology, 応用セラミックス研究所, 准教授 (50196408)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000)
Fiscal Year 2008: ¥1,560,000 (Direct Cost: ¥1,200,000、Indirect Cost: ¥360,000)
Fiscal Year 2007: ¥3,120,000 (Direct Cost: ¥2,400,000、Indirect Cost: ¥720,000)
|
|---|
| Keywords | 超高強度コンクリート / ひび割れ面性状 / せん断伝達特性 / 復元力特性 / 軸力 / せん断補強筋量 / 有限要素解析 / 離散ひび割れモデル / ひび割れ性状 / 膨張ひび割れ / 摩擦ひび割れ / 拘束力 |
|---|
| Research Abstract |
圧縮強度が100N/mm^2を超える超高強度コンクリートは粗骨材を貫通するひび割れが発生し,ひび割れ面は平滑になり,ひび割れ間のせん断力伝達能力が低下する。本研究では,超高強度コンクリート柱部材のせん断力-部材角履歴曲線の非対称性に関して,ひび割れ面の挙動とせん断伝達特性に基づいて,その現象のメカニズムを実験的,解析的に明らかにした。
|