Study on the magnetic anisotropy of a"-Fe1GN2 with nanostructured smaterials
| Project/Area Number |
19560661
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Physical properties of metals
|
|---|
| Research Institution | University of Tsukuba |
|---|
Principal Investigator |
KITA Eiji University of Tsukuba, 大学院・数理物質科学研究科, 教授 (80134203)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
YANAGIHARA Hideto 筑波大学, 大学院・数理物質科学研究科, 准教授 (50302386)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000)
Fiscal Year 2008: ¥1,560,000 (Direct Cost: ¥1,200,000、Indirect Cost: ¥360,000)
Fiscal Year 2007: ¥2,990,000 (Direct Cost: ¥2,300,000、Indirect Cost: ¥690,000)
|
|---|
| Keywords | 電子・磁気物性 / 鉄窒化物 / 強磁性 / 磁気異方性 / ナノ粒子 / 共沈法 / 均一沈殿法 / 鉄酸化物 / 磁気トルク / 微粒子 |
|---|
| Research Abstract |
稀少金属を含まない高磁気異方性を持つ強磁性材料として鉄窒化物α"-Fe_16N_2に着目し、磁気異方性評価のため、20nm単相微粒子を磁場中配向することにより高配向試料を作製した。トルク測定の詳細な解析により磁気異方性の大きさを評価し、K_U=6.1x10^<6>erg/cm^3を得た。さらに微粒子試料のサイズを拡大することによりバルク状試料を得る手法開発を試みた。130nm程度のγ'-Fe4N試料を得る手法として、窒化と還元を繰り返す多段窒化法を開発に成功した。
|