On the Crystallography and Nucleation of the Martensitic Transformation in Yttria doped Zirconia
| Project/Area Number |
19560666
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Physical properties of metals
|
|---|
| Research Institution | Tottori University |
|---|
Principal Investigator |
HAYAKAWA Motozo Tottori University, 大学院工学研究科, 教授 (60093621)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
ONDA Tetsuhiko 鳥取大学, 大学院工学研究科, 講師 (80273879)
AKAO Takahiro 鳥取大学, 大学院工学研究科, 助教 (70335503)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,290,000 (Direct Cost: ¥3,300,000、Indirect Cost: ¥990,000)
Fiscal Year 2008: ¥1,820,000 (Direct Cost: ¥1,400,000、Indirect Cost: ¥420,000)
Fiscal Year 2007: ¥2,470,000 (Direct Cost: ¥1,900,000、Indirect Cost: ¥570,000)
|
|---|
| Keywords | イットリア添加ジルコニア / マルテンサイト変態 / 変態温度 / 結晶粒径依存性 / 粒界応力 / 負荷応力 / 試料サイズ依存性 / シミュレーション / 核生成サイト / エンブリオ密度 |
|---|
| Research Abstract |
本研究ではジルコニアのマルテンサイト変態における結晶学および核生成に関する問題を扱った.結晶学に関しの研究は現在進行中である.核生成に関する問題の内,核生成サイトの分布密度に関する研究は既に論文(5.発表論文を参照) が出版されているので,ここでは核生成に及ぼす粒間応力および一軸不可応力の影響に関して述べる.
|