Effect of interface structures on melting and solidification behavior
| Project/Area Number |
19560671
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Physical properties of metals
|
|---|
| Research Institution | National Institute for Materials Science |
|---|
Principal Investigator |
SINGH Alok National Institute for Materials Science, 新構造材料センター, 主席研究員 (60354213)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
SOMEKAWA Hidetoshi 独立行政法人物質・材料研究機構, 新構造材料センター, 主任研究員 (50391222)
|
|---|
| Project Period (FY) |
2007 – 2009
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥3,120,000 (Direct Cost: ¥2,400,000、Indirect Cost: ¥720,000)
Fiscal Year 2008: ¥650,000 (Direct Cost: ¥500,000、Indirect Cost: ¥150,000)
Fiscal Year 2007: ¥2,470,000 (Direct Cost: ¥1,900,000、Indirect Cost: ¥570,000)
|
|---|
| Keywords | 準結晶 / 構造解析 / 界面 / 溶融 / 凝固 / 透過型電子顕微鏡 / 示差熱分析 : DSC / 示差熱分析:DSC |
|---|
| Research Abstract |
ビスマス、スズ、鉛を添加した準結晶相とマイクロクリスタル相の界面構造とその溶融・凝固挙動について調査した。ビスマス添加は、格子の膨張と溶融時に9Kの加熱現象を示した。スズ添加は、準結晶相とマッチングの良い界面構造を形成し、凝固時に数カ所の過冷現象を示した。これは核形成サイトの存在と密接な関係があることを確認した。最後に、鉛の添加は、7K融点を低下させることが分かった。
|