Structural evaluation and property control of local stress induced lead-free piezoelectric ceramics
| Project/Area Number |
19560675
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Inorganic materials/Physical properties
|
|---|
| Research Institution | Nagoya Institute of Technology |
|---|
Principal Investigator |
KAKIMOTO Ken-ichi Nagoya Institute of Technology, 大学院・工学研究科, 准教授 (40335089)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000)
Fiscal Year 2008: ¥910,000 (Direct Cost: ¥700,000、Indirect Cost: ¥210,000)
Fiscal Year 2007: ¥3,770,000 (Direct Cost: ¥2,900,000、Indirect Cost: ¥870,000)
|
|---|
| Keywords | 環境材料 / セラミックス / 電子・電気材料 / 誘電体物性 / 圧電体 / 無鉛圧電体 / 結晶構造 / 温度特性 / 内部応力 |
|---|
| Research Abstract |
圧電セラミックスの鉛フリー化が求められており、その有力候補材料であるニオブ酸リチウムナトリウムカリウム(LNKN)固溶体セラミックスの優れた圧電特性の起源に注目が集まっており、本研究では、この起源を調査した。その結果、優れた圧電特性にはセラミックス中の内部構造歪みが直接関わっており、この内部構造歪みの導入が鉛フリー圧電セラミックスの新たな物性制御の材料設計法として活かせるとの結論に達した。
|
Report
(3 results)
Research Products
(93 results)
-
-
-
-
-
-
[Journal Article] Processing of Piezoelectric (Li, Na, K)NbO_3 Porous Ceramics and (Li, Na, K)NbO_3/KNbO_3 Composite2008
Author(s)
K. Kakimoto, T. Imura, Y. Fukui, M. Kuno, K. Yamagiwa, T. Mitsuoka, K. Ohbayashi
-
Journal Title
Jpn. J. Appl. Phy Vol. 46, No. 10B
Pages: 7089-7093
Related Report
Peer Reviewed
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-