Preparation and orientation control of layered double hydroxide thin films by the sol-gel process with hot water treatment
| Project/Area Number |
19560680
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Inorganic materials/Physical properties
|
|---|
| Research Institution | Osaka Prefecture University |
|---|
Principal Investigator |
KIYOHARU Tadanaga Osaka Prefecture University, 大学院・工学研究科, 准教授 (90244657)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000)
Fiscal Year 2008: ¥1,950,000 (Direct Cost: ¥1,500,000、Indirect Cost: ¥450,000)
Fiscal Year 2007: ¥2,600,000 (Direct Cost: ¥2,000,000、Indirect Cost: ¥600,000)
|
|---|
| Keywords | ゾルゲル法 / 温水処理 / 層状複水酸化物 / ゾルーゲル法 / 陰イオン交換体 / 薄膜 / 炭酸イオン / イオン伝導性 / 電極材料 / ゾル-ゲル法 |
|---|
| Research Abstract |
ゾルゲル法で作製したMO-Al_2O_3(M=Mg, Co, Ni, Zn)系前駆体薄膜を、様々な塩を含む温水に浸漬させることにより、陰イオンが層間に挿入された層状複水酸化物微結晶が表面に析出した薄膜を作製した。本手法により、有機色素などの大きな有機分子が挿入された層状複水酸化物微結晶を基板上に容易に析出させることができた。遷移金属を含む薄膜は、電気化学素子の電極として動作することを確認した
|