Preparation and Characterization of Porous Optical Hydrogen Sensor with Well-Controlled Microstructure
| Project/Area Number |
19560685
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Inorganic materials/Physical properties
|
|---|
| Research Institution | Kurume National College of Technology |
|---|
Principal Investigator |
HAMAGAMI Jun-ichi Kurume National College of Technology, 材料工学科, 准教授 (30285100)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000)
Fiscal Year 2008: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
Fiscal Year 2007: ¥3,380,000 (Direct Cost: ¥2,600,000、Indirect Cost: ¥780,000)
|
|---|
| Keywords | 室温作動型オプティカル水素センサ / パラジウム / 多孔質膜 / コロイド結晶テンプレート法 / 微細構造制御 / 水素ガスセンサ / 室温水素検知 / マイクロ構造制御 / 高分子ビーズテンプレート法 / オプティカル水素センサ |
|---|
| Research Abstract |
水素は次世代のクリーンなエネルギー源として期待されている。一方、水素は爆発性を有する危険なガスであるため、安全・安心な水素エネルギー社会を構築するためには、高性能な水素ガスセンサを開発することが重要である。本研究では、水素によって薄膜材料の光学特性が変化することを利用したオプティカル水素センサの高性能化に関する研究を遂行した。センサ材料には、室温において水素の吸着・解離作用を有するパラジウム(Pd)を選択した。多孔化技術を用いてサブミクロンスケールの構造が高度に制御された多孔質Pd センサ素子を作製することに成功した。得られた素子は、室温において高い感度と優れた応答・回復特性ならびに耐久性を示すことを明らかにした。
|