Development of Extrusion Process at Low Temperature and High Speed for Magnesium Alloys prestrained by Torsion Working
Project/Area Number |
19560724
|
Research Category |
Grant-in-Aid for Scientific Research (C)
|
Allocation Type | Single-year Grants |
Section | 一般 |
Research Field |
Material processing/treatments
|
Research Institution | University of Toyama |
Principal Investigator |
FURUI Mitsuaki University of Toyama, 大学院・理工学研究部(工学), 准教授 (90262972)
|
Co-Investigator(Kenkyū-buntansha) |
AIDA Tetsuo 富山大学, 大学院・理工学研究部(工学), 准教授 (20283062)
|
Project Period (FY) |
2007 – 2008
|
Project Status |
Completed (Fiscal Year 2008)
|
Budget Amount *help |
¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000)
Fiscal Year 2008: ¥2,340,000 (Direct Cost: ¥1,800,000、Indirect Cost: ¥540,000)
Fiscal Year 2007: ¥2,210,000 (Direct Cost: ¥1,700,000、Indirect Cost: ¥510,000)
|
Keywords | 塑性加工 / ねじり調製 / 押出し / 温間圧縮変形特性 / 変形双晶 / 結晶粒微細化 / 押出し低温化 |
Research Abstract |
AZ31Bマグネシウム合金にねじり調製押出し加工を適用する場合の最適加工条件は、ねじり温度623K, 押出し温度523K, 押出し速度1mm/s となった。ねじり調製したAZ31Bマグネシウム合金は、押出しの実操業温度である623K より373Kもの押出し低温化を実現できる可能性を示したことが本研究の最大の成果である。
|