Fabrication and Characterization of Ferromagnetic Amorphous Alloy Nanowires Using Electrodeposition Technique
| Project/Area Number |
19560734
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Material processing/treatments
|
|---|
| Research Institution | Nagasaki University |
|---|
Principal Investigator |
OHGAI Takeshi Nagasaki University, 工学部, 准教授 (60253481)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
KAGAWA Akio 長崎大学, 工学部, 教授 (00093401)
MIZUMOTO Masayuki 長崎大学, 工学部, 助教 (90325671)
TAKAO Keizo 長崎大学, 工学部, 技術職員 (90380823)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000)
Fiscal Year 2008: ¥910,000 (Direct Cost: ¥700,000、Indirect Cost: ¥210,000)
Fiscal Year 2007: ¥3,770,000 (Direct Cost: ¥2,900,000、Indirect Cost: ¥870,000)
|
|---|
| Keywords | 電析 / めっき / ナノワイヤー / ナノピラー / 薄膜 / 磁性材料 / アモルファス / 非晶質合金 / ニッケル / パーマロイ / モリブデン / メンブレンフィルター |
|---|
| Research Abstract |
微結晶または非晶質状態となるNi-Mo(W)およびNi-Fe-Mo(W)合金、更に、各々の合金ナノワイヤーの電析条件と得られた合金の組成、結晶構造および軟磁気特性との関連性を調査した。作製した試料を、断面SEM観察およびTEM観察した結果、合金中のモリブデン含有率の増加に伴い結晶粒は微細化し、非晶質状態へと変化することがわかった。また、テンプレート中に、高アスペクト比のナノワイヤーが形成できることが判明した。合金化により、薄膜・ナノワイヤーともに保磁力が小さくなった。
|