Fabrication of Ni-W Bulk Nanocrystalline Materials
| Project/Area Number |
19560735
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Material processing/treatments
|
|---|
| Research Institution | Osaka Prefecture University |
|---|
Principal Investigator |
TAKIGAWA Yorinobu Osaka Prefecture University, 大学院・工学研究科, 准教授 (70382231)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
HIGASHI Kenji 大阪府立大学, 大学院・工学研究科, 教授 (50173133)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥3,120,000 (Direct Cost: ¥2,400,000、Indirect Cost: ¥720,000)
Fiscal Year 2008: ¥1,820,000 (Direct Cost: ¥1,400,000、Indirect Cost: ¥420,000)
Fiscal Year 2007: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
|
|---|
| Keywords | Ni-W合金 / バルクナノ結晶材料 / 電解析出法 / 均質化 / 電流密度最適化 / 浴組成最適化 / 粒界アモルファス相 / 粒界偏析 / 第一原理計算 / 粒界エネルギー / 偏析エネルギー |
|---|
| Research Abstract |
電解析出法により、(1)結晶粒径50nm以下、(2)粒界アモルファス相を含まない、(3)厚み2mm以上、(4)マクロポアの最少化を実現したNi-Wバルクナノ結晶材料の創製を試みた。電流密度、浴組成等を最適化することにより目標値を達成するとともに、硬度のばらつきが1%以下である非常に均質な材料創製に成功した。
|