| Project/Area Number |
19560736
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Material processing/treatments
|
|---|
| Research Institution | University of Hyogo |
|---|
Principal Investigator |
KOBUNE Masafumi University of Hyogo, 大学院・工学研究科, 准教授 (90240960)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
藤澤 浩訓 兵庫県立大学, 大学院・工学研究科, 助教 (30285340)
|
|---|
| Co-Investigator(Renkei-kenkyūsha) |
FUJISAWA Hironori 兵庫県立大学, 大学院・工学研究科, 准教授 (30285340)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥2,860,000 (Direct Cost: ¥2,200,000、Indirect Cost: ¥660,000)
Fiscal Year 2008: ¥910,000 (Direct Cost: ¥700,000、Indirect Cost: ¥210,000)
Fiscal Year 2007: ¥1,950,000 (Direct Cost: ¥1,500,000、Indirect Cost: ¥450,000)
|
|---|
| Keywords | 高圧アニール / 結晶制御 |
|---|
| Research Abstract |
常温スパッタ法により(001)配向(Bi0.5La0.5)(Ni0.5Ti0.5)O3 [BLNT]結晶核上に非晶質BLNT膜を作製し、等方高圧アニール(HIP)法により至適に調整された酸素分圧下で結晶化を行い、結晶核と同方向の配向性とペロブスカイト構造をもつBLNT薄膜の作製に成功した。作製した膜の諸特性(構造及び電気特性)評価を行い、すぐれた強誘電体であることを実証した
|