Development of Ni_3Al-based intermetallic foil catalysts
| Project/Area Number |
19560774
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Catalyst/Resource chemical process
|
|---|
| Research Institution | National Institute for Materials Science |
|---|
Principal Investigator |
XU Ya National Institute for Materials Science, 燃料電池材料センター, 主幹研究員 (00370304)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
DEMURA Masahiko 独立行政法人物質・材料研究機構, 燃料電池材料センター, 主任研究員 (10354177)
HIRANO Toshiyuki 独立行政法人物質・材料研究機構, 燃料電池材料センター, NIMS特別研究員 (90354183)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000)
Fiscal Year 2008: ¥1,690,000 (Direct Cost: ¥1,300,000、Indirect Cost: ¥390,000)
Fiscal Year 2007: ¥2,990,000 (Direct Cost: ¥2,300,000、Indirect Cost: ¥690,000)
|
|---|
| Keywords | 触媒調製化学 / 金属間化合物 / 水素製造触媒 / 表面化学処理 / 化学表面処理 / メタンの水蒸気改質 / Ni_3Al箔 / Ni_3Al金属間化合物箔 / 水素製造用触媒 / ナノ組織化 / 表面処理 |
|---|
| Research Abstract |
優れた耐熱箔材料であるNi_3Al基金属間化合物箔の水素製造用の触媒特性を向上させるため、複相ナノ組織化と表面化学処理の2つの手法を用い、Ni_3Al基複相箔の表面に高活性のNi微粒子が分散したナノ組織構造の創製を行った。これによりNi_3Al基箔の触媒特性を著しく改善することができた。Ni_3Al基箔は水素製造用高温マイクロリアクターの構造材と触媒の2役を兼ねることが可能であることが明らかになった。
|
Report
(3 results)
Research Products
(78 results)
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
[Presentation] Surface Characterization of Ni_3Al foil Catalyst by Hard X-ray Photoelectron Spectroscopy2008
Author(s)
Y. Xu, H. Yoshikawa, J. H. Jang, M. Demura, K. Kobayashi, S. Ueda, D. Nomoto, Y. Yamashita, D. M. Wee, T. Hirano
Organizer
The 14^<th> International Congress on Catalysis
Place of Presentation
COEX Convention Center Seoul, Korea
Related Report
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-
-