Development of corrosion monitoring method applicable to high subcritical and supercritical aqueous oxidation environment
| Project/Area Number |
19560822
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Recycling engineering
|
|---|
| Research Institution | Osaka Prefecture University |
|---|
Principal Investigator |
INOUE Hiroyuki Osaka Prefecture University, 大学院・工学研究科, 講師 (40203252)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥2,730,000 (Direct Cost: ¥2,100,000、Indirect Cost: ¥630,000)
Fiscal Year 2008: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000)
Fiscal Year 2007: ¥1,690,000 (Direct Cost: ¥1,300,000、Indirect Cost: ¥390,000)
|
|---|
| Keywords | 高温亜臨界水酸化 / SCWO / 電気化学ノイズ / 腐食モニタリング / 電位ノイズ / 超臨界水酸化 |
|---|
| Research Abstract |
これまで適当な手法が無かった、高温亜臨界ならびに超臨界水酸化環境での腐食モニタリングを、電位ノイズ法の適用によって実現することを試みた。380℃よりも低い高温亜臨界温度域では、汎用ステンレス鋼であるSUS304鋼、高耐食性のNi 基材料であるC-276のいずれの試験片でも、全面腐食ならびに局部腐食の発生を、測定された電位ノイズ信号の波形から検出できることを確認した。超臨界水酸化環境では、臨界点に近い400℃を除き、低pHかつ高酸化性の溶液中でも、SUS304鋼試験片に腐食の痕跡は認められず、また電位ノイズの信号の発生もなかった。
|