The clarification of elastic-plastic rheological characteristics based on measurements of oil film temperature and suggestion on the mechanism of oil film breakdown
| Project/Area Number |
19760102
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (B)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Design engineering/Machine functional elements/Tribology
|
|---|
| Research Institution | Kyushu University |
|---|
Principal Investigator |
八木 和行 Kyushu University, 大学院・工学研究院, 准教授 (50349841)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥3,640,000 (Direct Cost: ¥3,400,000、Indirect Cost: ¥240,000)
Fiscal Year 2008: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000)
Fiscal Year 2007: ¥2,600,000 (Direct Cost: ¥2,600,000)
|
|---|
| Keywords | 弾性流体潤滑 / レオロジー / 弾塑性 / 油膜厚さ / 温度 |
|---|
| Research Abstract |
本研究では,弾性流体潤滑状態において,潤滑油にアルコールを使用した際に出現する特異油膜形状に代表されるような高圧・高せん断場でのレオロジー特性を明らかにすることを目的に,油膜厚さと温度の計測を行った.その結果,アルコールの鎖長によって特異油膜形状が異なることがわかった.また,温度測定の結果,接触面の温度は極めて小さいことがわかり,このことから潤滑膜は接触域で圧力の影響のため固化を起こし,特異油膜形状の発生に寄与していることを実験的に裏付けることができた.
|