Order-disorder transformation and magnetic transformation of L1_0-type FePd alloy nanoparticles studied by transmission electron microscopy
| Project/Area Number |
19760459
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (B)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Physical properties of metals
|
|---|
| Research Institution | Tohoku University |
|---|
Principal Investigator |
SATO Kazuhisa Tohoku University, 金属材料研究所, 助教 (70314424)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥3,670,000 (Direct Cost: ¥3,400,000、Indirect Cost: ¥270,000)
Fiscal Year 2008: ¥1,170,000 (Direct Cost: ¥900,000、Indirect Cost: ¥270,000)
Fiscal Year 2007: ¥2,500,000 (Direct Cost: ¥2,500,000)
|
|---|
| Keywords | 微粒子 / クラスター / L1_0型規則構造 / FePdナノ粒子 / 規則不規則変態 / 粒径依存性 / 高分解能電子顕微鏡 / 球面収差補正 / HAADF-STEM / Zコントラスト / FePd / 合金ナノ粒子 / 磁気変態 / 透過電子顕微鏡法 / 電子回折 / サイズ効果 |
|---|
| Research Abstract |
硬質磁性FePdナノ粒子の規則不規則変態を透過電子顕微鏡法・電子回折法により詳細に調べた結果、相変態温度の粒径依存性、変態温度直上での短範囲規則構造、高温での不規則化過程、規則格子形成の臨界粒径と格子歪について新たな知見を得ることができた。これまで不明であったL1_0型規則合金ナノ粒子における規則不規則変態の粒径依存性を実験的に明らかにすることができた。
|