Quantitative measurement of second ordered optical nonlinearity in spatial selected crystallized glass by laser i rradiation
| Project/Area Number |
19760463
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (B)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Inorganic materials/Physical properties
|
|---|
| Research Institution | Nagaoka University of Technology |
|---|
Principal Investigator |
HONMA Tsuyoshi Nagaoka University of Technology, 工学部, 助教 (70447647)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥3,700,000 (Direct Cost: ¥3,400,000、Indirect Cost: ¥300,000)
Fiscal Year 2008: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
Fiscal Year 2007: ¥2,400,000 (Direct Cost: ¥2,400,000)
|
|---|
| Keywords | 結晶化ガラス / レーザー結晶化 / ニオブ酸リチウム / 第二高調波 / 光変調器 / 光導波路 / 結晶成長 / 顕微ラマン散乱 / レーザー加工 / 光機能ガラス / 形態制御 / 非線形光学 |
|---|
| Research Abstract |
本研究は、申請者らが独白に見いだしたレーザー誘起局所加熱によりガラス基板上に位置選択的に形成した結晶ラインパターンについて、その局所的な光非線形性(第二高調波発生)の定量的評価をすることを目的とし、高い光変換機能を有するフレスノイト型結晶、ニオブ酸リチウムラインパターンのガラスヘの形成と形態の評価、そして二次光非線形性の定量的評価を実施し、得られたラインパターンはいずれも単結晶的な成長を示し、導波路として機能することを見いだした。
|