Development of separation membrane system using ordered mesoporous carbons prepared direct triblock copolymer templating method
| Project/Area Number |
19860074
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (Start-up)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Properties in chemical engineering process/Transfer operation/Unit operation
|
|---|
| Research Institution | Kansai University |
|---|
Principal Investigator |
TANAKA Shunsuke Kansai University, 環境都市工学部, 助教 (20454598)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥3,115,000 (Direct Cost: ¥2,710,000、Indirect Cost: ¥405,000)
Fiscal Year 2008: ¥1,755,000 (Direct Cost: ¥1,350,000、Indirect Cost: ¥405,000)
Fiscal Year 2007: ¥1,360,000 (Direct Cost: ¥1,360,000)
|
|---|
| Keywords | メソポーラスカーボン / 薄膜化 / フェノール樹脂 / ブロック共重合体 / 熱可塑性樹脂 / 熱分解性高分子 / 有機-有機相互作用 / アルミナ支持体 / 薄膜 / レゾール樹脂 / 熱硬化性樹脂 / 一段階合成 |
|---|
| Research Abstract |
フェノール樹脂と熱分解性高分子の有機-有機相互作用を利用して規則性ナノ構造ポリマーを調製し、それを炭化することによってメソポーラスカーボンを調製した。管型多孔質アルミナ支持体および陽極酸化アルミナ基材を用いて形態の制御に取り組んだ。また、前駆溶液のエタノール濃度を調整することにより、周期性および細孔径の制御を行った。得られたメソポーラスカーボンは、規則的に配列した均一な細孔構造を有し、グラフェンの高い化学的安定性を有することからシリカ膜では適応できない分離への応用が期待できる。
|