Development of Testing Methodology for Evaluation of Fracture Resistance of Advanced Silicon Carbide Composites
| Project/Area Number |
19860089
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (Start-up)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Composite materials/Physical properties
|
|---|
| Research Institution | Japan Atomic Energy Agency |
|---|
Principal Investigator |
NOZAWA Takashi Japan Atomic Energy Agency, 核融合研究開発部門, 任期付研究員 (70455278)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥3,115,000 (Direct Cost: ¥2,710,000、Indirect Cost: ¥405,000)
Fiscal Year 2008: ¥1,755,000 (Direct Cost: ¥1,350,000、Indirect Cost: ¥405,000)
Fiscal Year 2007: ¥1,360,000 (Direct Cost: ¥1,360,000)
|
|---|
| Keywords | 炭化ケイ素基複合材料 / 破壊抵抗 / ノッチ感受性 / 損傷評価 / 非線形破壊力学 / セラミックス基複合材料 / SiC / SiC複合材料 / 亀裂進展過程 / サイズ効果 / Sic / Sic複合材料 |
|---|
| Research Abstract |
SiC/SiC複合材料の破損評価のための破壊抵抗試験法の高度化を目的に、破損エネルギーに占める非可逆エネルギーの寄与を分離・定量化する解析法を新たに考案し、正味の破壊抵抗を算出することに成功した。特に、亀裂進展挙動の評価により、SiC/SiC複合材料のノッチ鈍感性を特定し、応力とエネルギーの相関関係を明らかにした。さらに、本手法を適用することで、非主軸試験から主軸強度を予測する方法に一定の見通しを得た。
|