Photo-induced electron migration through the integrated intersurface of graded semiconductor nanosheets and mesoporous silica film
| Project/Area Number |
20043029
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research on Priority Areas
|
| Allocation Type | Single-year Grants |
|---|
| Review Section |
Science and Engineering
|
|---|
| Research Institution | Kanagawa Academy of Science and Technology |
|---|
Principal Investigator |
TAKAGI Katsuhiko Kanagawa Academy of Science and Technology, 専務理事 (60023264)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
TAKAGI Shinsuke 首都大学東京, 都市環境科学研究科, 准教授 (40281240)
SASAI Ryo 名古屋大学, 工学研究科, 講師 (60314051)
|
|---|
| Project Period (FY) |
2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥2,100,000 (Direct Cost: ¥2,100,000)
Fiscal Year 2008: ¥2,100,000 (Direct Cost: ¥2,100,000)
|
|---|
| Keywords | 光電荷分離 / 長寿命安定化 / チタニアナノシート / 積層構造 / 光エネルギー変換 / 長寿命電荷分離状態 / SPR電場蛍光増感 / アニオン交換性層状複水酸化物 / Layer-by-Layer法 |
|---|
| Research Abstract |
本研究計画に従って、積層系で観測される長寿命電荷分離系の量子効率向上のため、チタニア、ニオブ酸塩、チタノニオブ酸の順に積層した傾斜伝導電位を検討したが、大きな促進効果が見られなかった。さらに研究計画で予定している複合膜系の電荷分離量子効率改善の試みとして金ナノ粒子(AuNP)のSPR電場増強効果を検討した。アニオン性ゲスト種の導入のため、これまで用いていたメソポーラスシリカ(MPS)をアニオン交換性層状複水酸化物(LDH)ナノシートに変え、導入したAuNPとTCPPとの距離を制御し、TCPP増感剤の増感効率の改善を図った。上記の実現のために、AuNPがTCPPの光励起を増感する場合の最適な距離について検討した。Layer-by-Layer法によりLDH/ArSO_3H層(2nm/枚)を積層することによりAuNPとTCPPとの距離を制御し、その距離とTCPPの蛍光強度の相関を検討した結果、3層(6nm)以上で蛍光増強が観測されるようになり、9層(18nm)程度で増強効果は最大となることを明らかにした。
|