Development of Hydrogen Separation Membranes with Controlled Silica Network sizes by structured Alkoxides
| Project/Area Number |
20760517
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (B)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Properties in chemical engineering process/Transfer operation/Unit operation
|
|---|
| Research Institution | Hiroshima University |
|---|
Principal Investigator |
KANEZASHI Masakoto Hiroshima University, 大学院・工学研究科, 助教 (10467764)
|
|---|
| Project Period (FY) |
2008 – 2009
|
| Project Status |
Completed (Fiscal Year 2009)
|
| Budget Amount *help |
¥4,160,000 (Direct Cost: ¥3,200,000、Indirect Cost: ¥960,000)
Fiscal Year 2009: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
Fiscal Year 2008: ¥2,860,000 (Direct Cost: ¥2,200,000、Indirect Cost: ¥660,000)
|
|---|
| Keywords | 水素分離膜 / 構造化アルコキシド / ゾル-ゲル法 / 分子ふるい / ゾルゲル法 |
|---|
| Research Abstract |
Bis (triethoxysilyl) ethane (BTESE), which consists of Si-C-C-Si bonds, was used as a silica precursor to prepare organic-inorganic hybrid silica membranes with loose amorphous networks. Pore size distribution, as determined by single gas permeation, suggested BTESE-derived silica membranes had loose amorphous silica structures compared to TEOS-derived silica membranes due to the differences in the minimum units of silica networks; for example, BTESE-derived silica membranes showed high hydrogen permeance (0.5-2.0×10^<-5>mol・m^<-2>・s^<-1>・Pa^<-1>) with high selectivity of H_2 to SF_6 (H_2/SF_6 permselectivity: 1,000-30,000) and low H_2 to N_2 permselectivity (10-20).
|