Chemical Modification and Microstructure Control to obtain Amorphous LCPs for Device Applications

• Project/Area Number: 20K05134
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 26040:Structural materials and functional materials-related
• Research Institution: Oita University
• Principal Investigator: 氏家 誠司 大分大学, 理工学部, 教授 (40185004)
• Project Period (FY): 2020-04-01 – 2024-03-31
• Project Status: Granted (Fiscal Year 2020)
• Budget Amount: ¥4,290,000 (Direct Cost: ¥3,300,000、Indirect Cost: ¥990,000); Fiscal Year 2023: ¥780,000 (Direct Cost: ¥600,000、Indirect Cost: ¥180,000); Fiscal Year 2022: ¥1,170,000 (Direct Cost: ¥900,000、Indirect Cost: ¥270,000); Fiscal Year 2021: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000); Fiscal Year 2020: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
• Keywords: 全芳香族液晶ポリエステル / 化学修飾 / 微細構造制御 / 等方的配向 / 熱膨張率

Outline of Research at the Start

全芳香族液晶ポリエステル（LCPEs）は，次世代エレクトロニクスの基材としての量産化に向けて，異方性配向緩和のための微細構造とマクロ構造の制御が急務となっている．この問題に対しては，LCPEsの組成バランスやフィラーの混合，加工プロセスなどによって解決しようとすることが一般的である．しかし，次世代技術をより確実にするには基礎科学的なアプローチによる体系化が重要である．本研究では，LCPEsの異方性配向緩和を反応性高分子を用いたLCPEsに対する化学修飾と分子配向構造制御により実現する。