Development of a novel direct dental pulp-capping material using 4-META/MMA-TBB resin with nano hydroxyapatite
| Project/Area Number |
20K18538
|
|---|
| Research Category |
Grant-in-Aid for Early-Career Scientists
|
| Allocation Type | Multi-year Fund |
|---|
| Review Section |
Basic Section 57030:Conservative dentistry-related
|
|---|
| Research Institution | Kyushu University |
|---|
Principal Investigator |
|
|---|
| Project Period (FY) |
2020-04-01 – 2022-03-31
|
| Project Status |
Completed (Fiscal Year 2021)
|
| Budget Amount *help |
¥4,290,000 (Direct Cost: ¥3,300,000、Indirect Cost: ¥990,000)
Fiscal Year 2021: ¥2,080,000 (Direct Cost: ¥1,600,000、Indirect Cost: ¥480,000)
Fiscal Year 2020: ¥2,210,000 (Direct Cost: ¥1,700,000、Indirect Cost: ¥510,000)
|
|---|
| Keywords | 4-META/MMA-TBB resin / Nano hydroxyapatite / dental pulp stem cells / reparative dentin / direct pulp capping / 4-META/MMA-TBBレジン / nano hydroxyapatite / 歯髄幹細胞 / 修復象牙質 / 直接覆髄 / ナノハイドロキシアパタイト / naHAp |
|---|
| Outline of Research at the Start |
本研究では、4-META/MMA-TBBレジンとnaHApの特性を生かして、広範囲の露髄面に象牙芽細胞分化を生物学的に促し、緻密な修復象牙質形成を促進することができる新規直接覆髄材の開発を企図している。本研究から得られる結果は、これまでにない理想的な治癒を導く直接覆髄材創生の基盤となるものであり、将来的に歯髄を健康的に保ち歯牙の長期維持を可能とする新規直接覆髄材の開発へと繋がるものであると考えている。
|
| Outline of Final Research Achievements |
This study was to evaluate the dentin-adhesive 4-META/MMA-TBB resin including osteo-conductive nano hydroxyapatite as a novel direct pulp capping material. The 30% naHAp/SB showed a good sealing ability and biocompatibility as SB does, and also induced odontoblastic differentiation of human dental pulp stem cells through a CaSR-MEK/ERK pathway. In addition, 30% naHAp/SB sealed the pulp exposure site by inducing reparative dentin with dentin tubules in a rat artificail pulp exposure model. These results indicate that 30% naHAp/SB can be used as a novel direct pulp capping material.
|
| Academic Significance and Societal Importance of the Research Achievements |
これまでに歯質接着性を有した直接覆髄材は存在せず、辺縁漏洩による術後感染のリスクが存在する。本研究で開発した新規直接覆髄材は歯質接着性を有しており、辺縁漏洩のリスクを抑え長期的な予後を見込むことができる。また、材料の諸性質の解析に加えて、修復象牙質形成の主役となる歯髄幹細胞の象牙芽細胞様分化に及ぼす影響ならびにその細胞内シグナル経路の解明を行った。さらに、動物実験モデルでは良好な修復象牙質形成効果を認めており、今後臨床応用へと繋げていくことができると考えている。
|