純チタンにおける引張双晶変形の寸法効果の解明

Research Project

Project/Area Number 22K14146
Research Category

Grant-in-Aid for Early-Career Scientists

Allocation TypeMulti-year Fund
Review Section Basic Section 18010:Mechanics of materials and materials-related
Research InstitutionKyushu University

Principal Investigator

植木 翔平  九州大学, 工学研究院, 助教 (50880382)

Project Period (FY) 2022-04-01 – 2025-03-31
Project Status Granted (Fiscal Year 2023)
Budget Amount *help
¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000)
Fiscal Year 2024: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
Fiscal Year 2023: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000)
Fiscal Year 2022: ¥2,340,000 (Direct Cost: ¥1,800,000、Indirect Cost: ¥540,000)
Keywords寸法効果 / チタン / 引張双晶 / マイクロ力学試験 / 双晶変形 / 加工硬化
Outline of Research at the Start

金属材料のマクロな機械的性質を正確に理解し制御するために、マイクロスケール力学特性評価が世界中で精力的に取り組まれている。六方最密構造を有するチタンにおいて、1~10ミクロンのサイズ範囲で、圧縮双晶変形の寸法効果がすべり変形に比べて顕著になることが示されており、このことは新たな材料開発指針を構築するものとして注目されている。本研究では、1~10ミクロンサイズの試験片に対して評価可能な引張試験技術を確立し、チタンにおける引張双晶変形の寸法効果を解明することを目的とする。本研究で得られる成果は、国内外で重点的な戦略として掲げられている、トランススケール力学制御の構築に大きく貢献するものとなる。

Outline of Annual Research Achievements

本年度は、昨年度に確立した「代表寸法が1~10ミクロンサイズの角柱試験片を用いたSEM内引張試験の手法」を用いて、純チタン単結晶のc軸([0001])方向にほぼ平行に引張負荷する試験を実施した。引張試験片の代表寸法は2,5および10ミクロンのものを用いた。その結果、代表寸法が小さくなるにつれて引張強度が上昇する、いわゆる寸法効果が確認された。また、試験後のEBSD(電子線後方散乱回折)解析によって、引張双晶変形のバリアント特定にも成功した。これらの結果を基に、応力-ひずみ曲線と変形組織との対応をとると、変形双晶の発生する応力レベルが代表寸法によって変化することが示唆された。

Current Status of Research Progress
Current Status of Research Progress

2: Research has progressed on the whole more than it was originally planned.

Reason

当初の予定していた実験を実施でき、その後の解析も順調に行えたことから、おおむね順調に進展していると判断した。

Strategy for Future Research Activity

当初の予定通り、[0001]方向に対して垂直に引張負荷する試験を実施する。

Report

(2 results)
  • 2023 Research-status Report
  • 2022 Research-status Report
  • Research Products

    (3 results)

All 2024 2022

All Journal Article (2 results) (of which Int'l Joint Research: 1 results,  Peer Reviewed: 2 results,  Open Access: 1 results) Presentation (1 results)

  • [Journal Article] Effects of crystallographic orientation and lamellar configuration on fatigue crack propagation in single-colony structures of Ti?6Al?4V alloy: Alternating shear crack growth vs. damage accumulation crack propagation2024

    • Author(s)
      Ueki Shohei、Mine Yoji、Chiu Yu-Lung、Bowen Paul、Takashima Kazuki
    • Journal Title

      Materials Science and Engineering: A

      Volume: 890 Pages: 145885-145885

    • DOI

      10.1016/j.msea.2023.145885

    • Related Report
      2023 Research-status Report
    • Peer Reviewed / Int'l Joint Research
  • [Journal Article] Comparative Study of Shear Fracture between Fe-based Amorphous and Ultrafine-grained Alloys Using Micro-tensile Testing2022

    • Author(s)
      Yuki Tampa, Kosuke Takagi, Shohei Ueki, Motoki Ohta, Yoji Mine, Kazuki Takashima
    • Journal Title

      ISIJ International

      Volume: 62 Issue: 8 Pages: 1741-1749

    • DOI

      10.2355/isijinternational.ISIJINT-2022-088

    • ISSN
      0915-1559, 1347-5460
    • Year and Date
      2022-08-15
    • Related Report
      2022 Research-status Report
    • Peer Reviewed / Open Access
  • [Presentation] Ti-6Al-4Vラメラ合金単一コロニーにおける交互せん断疲労き裂進展と損傷蓄積疲労き裂伝播2024

    • Author(s)
      植木翔平、峯洋二、Yu-Lung Chiu、Paul Bowen、高島和希
    • Organizer
      日本鉄鋼協会第187回春季講演大会
    • Related Report
      2023 Research-status Report

URL: 

Published: 2022-04-19   Modified: 2024-12-25  

Information User Guide FAQ News Terms of Use Attribution of KAKENHI

Powered by NII kakenhi