| Project/Area Number |
22K17127
|
|---|
| Research Category |
Grant-in-Aid for Early-Career Scientists
|
| Allocation Type | Multi-year Fund |
|---|
| Review Section |
Basic Section 57050:Prosthodontics-related
|
|---|
| Research Institution | Tohoku University |
|---|
Principal Investigator |
Katsuda Yusuke 東北大学, 歯学研究科, 非常勤講師 (70781277)
|
|---|
| Project Period (FY) |
2022-04-01 – 2024-03-31
|
| Project Status |
Completed (Fiscal Year 2023)
|
| Budget Amount *help |
¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000)
Fiscal Year 2023: ¥2,210,000 (Direct Cost: ¥1,700,000、Indirect Cost: ¥510,000)
Fiscal Year 2022: ¥2,340,000 (Direct Cost: ¥1,800,000、Indirect Cost: ¥540,000)
|
|---|
| Keywords | CAD/CAM冠 / 接着性レジンセメント / 破折強度 / 熱分析 / 脱離 |
|---|
| Outline of Research at the Start |
CAD/CAM冠は装着後早期の脱離の問題が取りざたされ、申請者らは接着破壊の要因として冠および支台歯の変形によるセメント界面の疲労があることを示した。このことはCAD/CAM冠のトラブルを防ぐにあたり、変形の挙動をより詳細に把握することが重要である可能性を示している。本研究では形状の異なる支台歯やクラウンによる荷重時の変形量の違いを実測し、形態からクラウンのひずみ量の予測をすることを目的としている。また、この目的達成のためには、AIによる機械学習の技術を用いて、より精度の高い予測方法の確立を目指す。
|
| Outline of Final Research Achievements |
The purpose of this study was to evaluate the abutment tooth morphology for the occurrence of CAD/CAM composite resin crown problems and to assess the predictability of dehiscence. Factors affecting the prognosis of CAD/CAM composite resin crowns were investigated by focusing on cement and abutment tooth materials and their differences, and by evaluating crown deformation under load.
The study examined conditions such as abutment tooth material, adhesive resin cement type, and cement thickness, and suggested that these conditions affect the failure of the crown material. The polymerization conditions of the adhesive resin cement could also affect the modulus of elasticity and the fracture strength of the crown materials. In this study, the degree of polymerization of resin was evaluated by thermal analysis. The results were generally reasonable, and the method is expected to be used to evaluate the degree of polymerization from a new perspective in the future.
|
| Academic Significance and Societal Importance of the Research Achievements |
CAD/CAMレジン冠の脱離トラブルの抑制のためには、これまで接着に注目した研究が多く報告されてきたが、クラウンの弾性係数やひずみに着目した報告は少ない。本研究ではCAD/CAMレジン冠の支台歯の条件や接着性レジンセメントの種類、セメント厚み、重合度に着目し、それらの条件の違いによりクラウン・セメント・支台歯の複合的な変形に影響する可能性が示唆され、予後に影響し得ることが示された。また今回熱分析によるレジンの重合度の評価を試み、新たな観点からの重合度の評価方法として期待されることを示した。
|