Development of novel tooth restorative material with similar wear property as human enamel

Research Project

Project/Area Number 22K20999
Research Category

Grant-in-Aid for Research Activity Start-up

Allocation TypeMulti-year Fund
Review Section 0907:Oral science and related fields
Research InstitutionKyushu Dental College

Principal Investigator

Tokunaga Jumpei  九州歯科大学, 歯学部, 特別研修員 (00966658)

Project Period (FY) 2022-08-31 – 2024-03-31
Project Status Completed (Fiscal Year 2023)
Budget Amount *help
¥2,860,000 (Direct Cost: ¥2,200,000、Indirect Cost: ¥660,000)
Fiscal Year 2023: ¥1,430,000 (Direct Cost: ¥1,100,000、Indirect Cost: ¥330,000)
Fiscal Year 2022: ¥1,430,000 (Direct Cost: ¥1,100,000、Indirect Cost: ¥330,000)
KeywordsCAD/CAM / 摩耗 / エナメル質 / 生体模倣 / 歯 / 歯冠修復
Outline of Research at the Start

クラウンなどの修復物と対合歯は咀嚼などによって摩耗する。材料の種類によっては、対合歯または材料自体の損傷が大きくなり、予後不良を招く恐れがある。そのため、エナメル質/材料または材料/材料間の摩耗性は重要である。しかし、既存のあらゆる材料において、エナメル質と同等の摩耗性をもつ修復物は存在しない。そこで本研究では、エナメル質と同じ摩耗性をもつ歯冠修復用CAD/CAMブロックを開発することを目的とする。具体的には、申請者らが合成に成功したエナメル質と同じ硬さをもつ新素材に改良を加え、実現を目指す。

Outline of Final Research Achievements

The aim of this study was to develop a novel polymer-infiltrated ceramic network (PICN) material for mimicking tooth wear characteristics. The PICN was fabricated d by polymer-infiltration and its polymerization. The wear properties of the PICN was evaluated in a two-body wear testing machine. The wear volume of the PICN was higher than that of commercially available PICN and lower than that of zirconia ceramic. These results suggested that the PICN may be relatively similar to the wear properties of enamel.

Academic Significance and Societal Importance of the Research Achievements

本研究により、新規ポリマー含浸セラミックスの摩耗性が歯質に近い可能性があることが示された。この研究で得られた知見をもとに、新規歯冠修復用材料が開発されれば、天然歯に近い修復処置が可能となると考えられる。

Report

(3 results)
  • 2023 Annual Research Report   Final Research Report ( PDF )
  • 2022 Research-status Report

URL: 

Published: 2022-09-01   Modified: 2025-01-30  

Information User Guide FAQ News Terms of Use Attribution of KAKENHI

Powered by NII kakenhi