| Project/Area Number |
22KF0181
|
|---|
| Project/Area Number (Other) |
21F21705 (2021-2022)
|
|---|
| Research Category |
Grant-in-Aid for JSPS Fellows
|
| Allocation Type | Multi-year Fund (2023)
Single-year Grants (2021-2022) |
|---|
| Section | 外国 |
|---|
| Review Section |
Basic Section 90110:Biomedical engineering-related
|
|---|
| Research Institution | Kyoto University |
|---|
Principal Investigator |
小松 直樹 京都大学, 人間・環境学研究科, 教授 (30253008)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
CHEN XIAOXIAO 京都大学, 人間・環境学研究科, 外国人特別研究員
|
|---|
| Project Period (FY) |
2023-03-08 – 2024-03-31
|
| Project Status |
Completed (Fiscal Year 2023)
|
| Budget Amount *help |
¥2,300,000 (Direct Cost: ¥2,300,000)
Fiscal Year 2023: ¥400,000 (Direct Cost: ¥400,000)
Fiscal Year 2022: ¥1,100,000 (Direct Cost: ¥1,100,000)
Fiscal Year 2021: ¥800,000 (Direct Cost: ¥800,000)
|
|---|
| Keywords | 磁性酸化鉄 / ナノ粒子 / 温熱効果 / 癌 / 治療 / 光 / 光温熱療法 / 鉄 / ポリグリセロール / 光温熱効果 / 酸化鉄 |
|---|
| Outline of Research at the Start |
鉄を担持したポリグリセロールで化学修飾されたナノ粒子を光、あるいは磁気増感剤とするがん治療法について検討を行う。その際、ナノ粒子のポリグリセロールによる化学修飾と鉄の担持を含むナノ製剤の合成から、腫瘍細胞を用いた in vitro での毒性試験や薬効評価, 腫瘍細胞を皮下に移植した担がんマウスを用いた in vivo での腫瘍成長抑制効果、体内動態評価、そして、安全性評価などの一連の実験を全て、当研究室で行う。
|
| Outline of Annual Research Achievements |
2021年度において、超磁性酸化鉄ナノ粒子(SPION)を PG で修飾した SPION-PG を合成し、癌増殖抑制作用を in vitro にて評価したが、特に優れた細胞増殖抑制効果は見られなかった。そのため、同じく in vitro にて光照射下や磁場中での温熱効果について検討を行ったところ、どちらも優れた効果が見られた。
2022年度では、まず、SPION-PG のより詳細な分析を行った。具体的には、ナノ粒子中の鉄分の定量や熱重量分析、電子顕微鏡分析、さら には、SQUID による磁性測定を行い、これまでに報告されてきたSPIONに比べ、より優れた磁場中での温熱効果を確認し、その原因を明らかにした。
最終年度である2023年度は担癌マウスを用いた in vivo において、腫瘍成長抑制効果について検討を行った。具体的には、京都大学環境安全保健機構放射線管理部門（RIセンター）にて、まず、マウス大腸癌細胞株CT26を移植したマウスを作成し、次に、 SPION-PG を尾静脈から導入一定時間後に光を照射し、光療法による癌の治療を試み、さらに、酸化鉄ナノ粒子の磁場中での発熱に基づく治療について、検討した。後者については、in vitro である水中では発熱が見られたものの、生体中においては、顕著な発熱が全く見られず、残念ながら、顕著な腫瘍成長抑制効果を確認するには至らなかった。これは、血液をはじめとする体液の粘性の高さに原因があると考えている。
|