Composite electrodes of iron oxides and carbons for high rate electrochemical reactions of lithium-oxygen batteries
| Project/Area Number |
23656603
|
|---|
| Research Category |
Grant-in-Aid for Challenging Exploratory Research
|
| Allocation Type | Multi-year Fund |
|---|
| Research Field |
Energy engineering
|
|---|
| Research Institution | The University of Tokyo |
|---|
Principal Investigator |
HIBINO Mitsuhiro 東京大学, 大学院・工学系研究科, 研究員 (20270910)
|
|---|
| Project Period (FY) |
2011 – 2012
|
| Project Status |
Completed (Fiscal Year 2012)
|
| Budget Amount *help |
¥3,770,000 (Direct Cost: ¥2,900,000、Indirect Cost: ¥870,000)
Fiscal Year 2012: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000)
Fiscal Year 2011: ¥2,730,000 (Direct Cost: ¥2,100,000、Indirect Cost: ¥630,000)
|
|---|
| Keywords | エネルギー生成 / 変換 / 空気電池 / 二次電池 / 複合体電極 / 電気化学触媒 |
|---|
| Research Abstract |
Composite electrode materials of iron-based oxides and carbons for lithium-air batteries were investigated. Among various iron-based oxides investigated inthis study, perovskite-related A_0.5La_0.5FeO_z（A = Ca, Sr）underwent extraction and insertion of oxideions stably in wide range of oxygen composit~ion. Because of it allows reversible and repeatable extraction/reinsertion of oxide ions at fast rate ( D = 1.2×10^-13 cm^2 s^-1), Ca_0.5La_0.5FeO_2.863 was foundto be expected as an oxygen reduction catalyst (or a mediator) for air electrode of lithium-air batteries.
|