Vildation of Evaluating Fatigue Strength of Carbon Fiber Reinforced Plastic Laminates by Using Ulatrasonic Fatigue Testing Methd

• Project/Area Number: 23K03572
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 18010:Mechanics of materials and materials-related
• Research Institution: Shizuoka University
• Principal Investigator: 島村 佳伸 静岡大学, 工学部, 教授 (80272673)
• Co-Investigator(Kenkyū-buntansha): 藤井 朋之 静岡大学, 工学部, 准教授 (30377840)
• Project Period (FY): 2023-04-01 – 2026-03-31
• Project Status: Granted (Fiscal Year 2023)
• Budget Amount: ¥4,810,000 (Direct Cost: ¥3,700,000、Indirect Cost: ¥1,110,000); Fiscal Year 2025: ¥520,000 (Direct Cost: ¥400,000、Indirect Cost: ¥120,000); Fiscal Year 2024: ¥520,000 (Direct Cost: ¥400,000、Indirect Cost: ¥120,000); Fiscal Year 2023: ¥3,770,000 (Direct Cost: ¥2,900,000、Indirect Cost: ¥870,000)
• Keywords: 炭素繊維強化プラスチック / 超音波疲労試験法 / 疲労強度

Outline of Research at the Start

本研究では，実用で広く使われている擬似等方性積層板を主な対象として，実用環境によくみられる引張の平均応力が作用する場合について，超音波疲労試験と油圧サーボ式疲労試験の結果の比較検討を実施してひずみ速度の違いが疲労強度に及ぼす影響を検討し，さらにその影響が大きい場合は分子構造レベルでの損傷蓄積過程とミクロからメゾスケールの損傷発達過程に着目することで，その原因解明にも取り組む．