サーフェスデザイナブルMg合金の創製

• Project/Area Number: 23K23103
• Project/Area Number (Other): 22H01835 (2022-2023)
• Research Category: Grant-in-Aid for Scientific Research (B)
• Allocation Type: Multi-year Fund (2024); Single-year Grants (2022-2023)
• Section: 一般
• Review Section: Basic Section 26050:Material processing and microstructure control-related
• Research Institution: National Institute for Materials Science
• Principal Investigator: 光延 由希子 (小川由希子) 国立研究開発法人物質・材料研究機構, 構造材料研究センター, 主任研究員 (70814268)
• Project Period (FY): 2022-04-01 – 2027-03-31
• Project Status: Granted (Fiscal Year 2024)
• Budget Amount: ¥17,680,000 (Direct Cost: ¥13,600,000、Indirect Cost: ¥4,080,000); Fiscal Year 2027: ¥2,730,000 (Direct Cost: ¥2,100,000、Indirect Cost: ¥630,000); Fiscal Year 2026: ¥3,250,000 (Direct Cost: ¥2,500,000、Indirect Cost: ¥750,000); Fiscal Year 2025: ¥2,860,000 (Direct Cost: ¥2,200,000、Indirect Cost: ¥660,000); Fiscal Year 2024: ¥825,562 (Direct Cost: ¥635,048、Indirect Cost: ¥190,514); Fiscal Year 2023: ¥2,860,000 (Direct Cost: ¥2,200,000、Indirect Cost: ¥660,000); Fiscal Year 2022: ¥8,840,000 (Direct Cost: ¥6,800,000、Indirect Cost: ¥2,040,000)
• Keywords: マグネシウム合金 / 耐食性 / 意匠性 / 撥水性 / 陽極酸化

Outline of Research at the Start

Mgは実用金属上最軽量であるにもかかわらず、低い強度・延性・耐食性からその用途は限られている。耐食性の担保については、一般に表面処理の後塗装を行う多段階の工程を必要としてきた。本研究では、Mg-Sc合金において酸化工程のみで形成可能な皮膜を利用し表面を適切にデザインすることで、塗装等多段階に渡る表面処理が不要な、高耐食性・意匠性・撥水性を兼ね備えるMg合金の実現を目指す。