Bond percolationゲルによる網目構造と力学物性の相関解明

Research Project

Project/Area Number	23K23403
Project/Area Number (Other)	22H02135 (2022-2023)
Research Category	Grant-in-Aid for Scientific Research (B)
Allocation Type	Multi-year Fund (2024) Single-year Grants (2022-2023)
Section	一般
Review Section	Basic Section 35020:Polymer materials-related
Research Institution	Hokkaido University
Principal Investigator	Li Xiang 北海道大学, 先端生命科学研究院, 准教授 (30759840)
Project Period (FY)	2022-04-01 – 2027-03-31
Project Status	Granted (Fiscal Year 2024)
Budget Amount *help	¥17,160,000 (Direct Cost: ¥13,200,000、Indirect Cost: ¥3,960,000) Fiscal Year 2026: ¥3,250,000 (Direct Cost: ¥2,500,000、Indirect Cost: ¥750,000) Fiscal Year 2025: ¥3,380,000 (Direct Cost: ¥2,600,000、Indirect Cost: ¥780,000) Fiscal Year 2024: ¥3,380,000 (Direct Cost: ¥2,600,000、Indirect Cost: ¥780,000) Fiscal Year 2023: ¥3,640,000 (Direct Cost: ¥2,800,000、Indirect Cost: ¥840,000) Fiscal Year 2022: ¥3,510,000 (Direct Cost: ¥2,700,000、Indirect Cost: ¥810,000)
Keywords	ゲル / 高分子 / 変形 / 構造解析 / 構造 / 小角散乱 / 広角散乱
Outline of Research at the Start	ゲルはその巨大な高分子網目のおかげで、多くの溶媒を保持しながら、弾性的に大きく変形できるという特徴的な物性を持つ。しかし、確率論的に形成される乱雑な網目構造によって、構造と力学物性の相関を理解することがいまだに困難である。本研究では、近年申請者らが開発したボンドパー子レーション条件で作られる超均一ゲルをモデル材料として用いて、ゲルを大きく変形させた際の構造と力学物性の系統的な評価し、ゲルのマクロな力学挙動とミクロな構造変化の相関を解明していく。