Electrochemical epitaxial growth of lithium metal

• Project/Area Number: 23K23451
• Project/Area Number (Other): 22H02183 (2022-2023)
• Research Category: Grant-in-Aid for Scientific Research (B)
• Allocation Type: Multi-year Fund (2024); Single-year Grants (2022-2023)
• Section: 一般
• Review Section: Basic Section 36020:Energy-related chemistry
• Research Institution: Hokkaido University
• Principal Investigator: 松井 雅樹 北海道大学, 理学研究院, 教授 (70639210)
• Project Period (FY): 2022-04-01 – 2026-03-31
• Project Status: Granted (Fiscal Year 2024)
• Budget Amount: ¥17,810,000 (Direct Cost: ¥13,700,000、Indirect Cost: ¥4,110,000); Fiscal Year 2025: ¥2,080,000 (Direct Cost: ¥1,600,000、Indirect Cost: ¥480,000); Fiscal Year 2024: ¥910,000 (Direct Cost: ¥700,000、Indirect Cost: ¥210,000); Fiscal Year 2023: ¥3,380,000 (Direct Cost: ¥2,600,000、Indirect Cost: ¥780,000); Fiscal Year 2022: ¥9,360,000 (Direct Cost: ¥7,200,000、Indirect Cost: ¥2,160,000)
• Keywords: 結晶成長 / ファセット面 / 電析 / リチウム金属 / 蓄電池 / 負極 / エピタキシャル成長

Outline of Research at the Start

本研究では，リチウム金属負極がウィスカー状に形成されるという問題を本質的に解決するための手段として，基板とリチウム金属の化学的な親和性に着目し，その結晶成長方位の制御を目指すものである．リチウムと化学的に親和性の高い金属基板を選択することで，基板の面に沿った二次元成長の促進が期待される．本研究では，リチウム金属の二次元成長を実現する基板材料の探索と，その結晶成長過程の解析を実施する．