| Project/Area Number |
23K26588
|
|---|
| Project/Area Number (Other) |
23H01895 (2023)
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Multi-year Fund (2024)
Single-year Grants (2023) |
|---|
| Section | 一般 |
|---|
| Review Section |
Basic Section 31010:Nuclear engineering-related
|
|---|
| Research Institution | Yokohama National University |
|---|
Principal Investigator |
大野 直子 横浜国立大学, 大学院工学研究院, 准教授 (40512489)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
余 浩 東北大学, 金属材料研究所, 助教 (10825871)
笠田 竜太 東北大学, 金属材料研究所, 教授 (20335227)
近藤 正聡 東京工業大学, 科学技術創成研究院, 准教授 (70435519)
|
|---|
| Project Period (FY) |
2023-04-01 – 2026-03-31
|
| Project Status |
Granted (Fiscal Year 2024)
|
| Budget Amount *help |
¥19,110,000 (Direct Cost: ¥14,700,000、Indirect Cost: ¥4,410,000)
Fiscal Year 2025: ¥3,900,000 (Direct Cost: ¥3,000,000、Indirect Cost: ¥900,000)
Fiscal Year 2024: ¥3,900,000 (Direct Cost: ¥3,000,000、Indirect Cost: ¥900,000)
Fiscal Year 2023: ¥11,310,000 (Direct Cost: ¥8,700,000、Indirect Cost: ¥2,610,000)
|
|---|
| Keywords | 鉛冷却小型モジュール炉 / 液体金属脆化 / 引張試験 / FeCrAl-ODS / 重畳環境 |
|---|
| Outline of Research at the Start |
第4世代原子炉である鉛冷却高速炉(LFR)について、炉心構造材に保護性のアルミナ被膜を自己形成するFeCrAl系の酸化物分散強化合金(FeCrAl-ODS)を用いることで、液体金属脆化を克服することを目指す。液体金属腐食と引張応力が重畳する環境での機械特性評価が簡単に行え、且つ重畳環境の影響を解析可能な試験のレイアウトを新たに考案した。フェライト系FeCrAl-ODSおよびオーステナイト系FeCrAl-ODSに我々の考案したレイアウトを適用して、液体金属腐食環境での試験を実施し、液体金属脆化感受性・アルミナ被膜の自己形成可能性を評価することで、FeCrAl-ODSのLFRへの適用性を判断する。
|