側鎖官能基の密集と主鎖の高配向性を特徴とした液晶性ポリ置換メチレンの機能発現

• Project/Area Number: 23K26713
• Project/Area Number (Other): 23H02020 (2023)
• Research Category: Grant-in-Aid for Scientific Research (B)
• Allocation Type: Multi-year Fund (2024); Single-year Grants (2023)
• Section: 一般
• Review Section: Basic Section 35020:Polymer materials-related
• Research Institution: Tokyo Institute of Technology
• Principal Investigator: 戸木田 雅利 東京工業大学, 物質理工学院, 教授 (30301170)
• Project Period (FY): 2023-04-01 – 2027-03-31
• Project Status: Granted (Fiscal Year 2024)
• Budget Amount: ¥18,590,000 (Direct Cost: ¥14,300,000、Indirect Cost: ¥4,290,000); Fiscal Year 2026: ¥5,460,000 (Direct Cost: ¥4,200,000、Indirect Cost: ¥1,260,000); Fiscal Year 2025: ¥5,460,000 (Direct Cost: ¥4,200,000、Indirect Cost: ¥1,260,000); Fiscal Year 2024: ¥3,640,000 (Direct Cost: ¥2,800,000、Indirect Cost: ¥840,000); Fiscal Year 2023: ¥4,030,000 (Direct Cost: ¥3,100,000、Indirect Cost: ¥930,000)
• Keywords: 高分子液晶 / ポリ置換メチレン / イオン液体 / イオン伝導

Outline of Research at the Start

電荷輸送特性やイオン伝導性を持ち合わせた液晶性機能分子が設計されてきた．液晶機能分子の機能性は液晶構造を形成するメソゲンに付与されるため，別の機能性を持たせようとすると，メソゲンの設計からやり直しになり，液晶性発現が困難になる場合が多い．また，液晶機能分子の高分子化も困難である．本研究は，ポリ置換メチレン（PM）を基盤に，機能性を側鎖に導入した官能基に，液晶形成を主鎖に担わせ，同一の分子設計指針で様々な機能性を付与でき，かつ高分子が高配向した単結晶的単一ドメインが調製できる「液晶性機能高分子」を創製する．