Novel synthesis of sol-gel derived mesostructures for controlling their electro chemical behaviors
| Project/Area Number |
24750206
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (B)
|
| Allocation Type | Multi-year Fund |
|---|
| Research Field |
Inorganic industrial materials
|
|---|
| Research Institution | Osaka Prefecture University |
|---|
Principal Investigator |
TOKUDOME Yasuaki 大阪府立大学, 工学(系)研究科(研究院), 助教 (50613296)
|
|---|
| Project Period (FY) |
2012-04-01 – 2014-03-31
|
| Project Status |
Completed (Fiscal Year 2013)
|
| Budget Amount *help |
¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000)
Fiscal Year 2013: ¥1,560,000 (Direct Cost: ¥1,200,000、Indirect Cost: ¥360,000)
Fiscal Year 2012: ¥2,990,000 (Direct Cost: ¥2,300,000、Indirect Cost: ¥690,000)
|
|---|
| Keywords | ゾル－ゲル / 薄膜 / カーボン / メソポーラス / 親水化 / ナノ構造 / 多孔性材料 / カーボン系材料 |
|---|
| Research Abstract |
Mesoporous carbon films were prepared via a process that allows coating on various substrates, including metals. The mesomorphology can be controlled by changing starting composition in an appropriately-designed reaction system. Systematic characterizations have revealed that the obtained carbons exhibit structure-induced hydrophilization depending on the mesomorphology. Chemically-modified hydrophilic carbons are well known to facilitate an electrode reaction in a polar system. The materials obtained here potentially provide the similar effect.
|