A study on the interfaces of transition-metal oxides with low valence and metastable structures by the electrochemical modulation of electronics states for exploring their functionality

• Project/Area Number: 24H00480
• Research Category: Grant-in-Aid for Scientific Research (A)
• Allocation Type: Single-year Grants
• Section: 一般
• Review Section: Medium-sized Section 36:Inorganic materials chemistry, energy-related chemistry, and related fields
• Research Institution: Institute of Science Tokyo
• Principal Investigator: 大友 明 東京工業大学, 物質理工学院, 教授 (10344722)
• Project Period (FY): 2024-04-01 – 2027-03-31
• Project Status: Granted (Fiscal Year 2024)
• Budget Amount: ¥49,140,000 (Direct Cost: ¥37,800,000、Indirect Cost: ¥11,340,000); Fiscal Year 2025: ¥11,180,000 (Direct Cost: ¥8,600,000、Indirect Cost: ¥2,580,000); Fiscal Year 2024: ¥29,510,000 (Direct Cost: ¥22,700,000、Indirect Cost: ¥6,810,000)
• Keywords: 薄膜電子材料 / エピタキシー / 電気化学 / 界面物性 / 超伝導材料・素子

Outline of Research at the Start

研究代表者らは，リチウムイオンの電気化学な脱挿入に伴うキャリアドープを酸化物に適用すると，さまざまな電子相転移が引き起こされることを明らかにしてきた。本研究では，多様な結晶構造や原子価をとる遷移金属酸化物の準安定相を積層した構造を薄膜技術によって作製し，積層構造の界面における電子状態を電気化学セル中でその場観測・解析し，新奇なふるまいの実証とそれらの機能開拓を目的とする。また，これにより新たな電気伝導性，磁性，光学特性を発現する界面構造の創製を目指す。